SPESIFIKASI STANDARD TIUB GELENGKEL KELULI TAHAN KARAT
321 keluli tahan karat tiub bergelung 6*1mm
| Standard | ASTM A213 (Dinding Purata) dan ASTM A269 |
| Tiub Gegelung Keluli Tahan Karat Diameter Luar | 1/16" hingga 3/4" |
| Ketebalan Tiub Gegelung Keluli Tahan Karat | .010″ Melalui .083” |
| Gred Tiub Gegelung Keluli Tahan Karat | SS 201, SS 202, SS 304, SS 304L, SS 309, SS 310, SS 316, SS 316L, SS 317L, SS 321, SS 347, SS 904L |
| Saiz Rnage | 5/16, 3/4, 3/8, 1-1/2, 1/8, 5/8, 1/4, 7/8, 1/2, 1, 3/16 inci |
| Kekerasan | Mikro dan Rockwell |
| Toleransi | D4/T4 |
| Kekuatan | Pecah dan Tegang |
GRED SETARA TUBUNG GELENG KELULI KELULI STAINLESS
321 keluli tahan karat tiub bergelung 6*1mm
| STANDARD | WERKSTOFF NR. | UNS | JIS | BS | GOST | AFNOR | EN |
|---|---|---|---|---|---|---|---|
| SS 304 | 1.4301 | S30400 | SUS 304 | 304S31 | 08Х18Н10 | Z7CN18‐09 | X5CrNi18-10 |
| SS 304L | 1.4306 / 1.4307 | S30403 | SUS 304L | 3304S11 | 03Х18Н11 | Z3CN18–10 | X2CrNi18-9 / X2CrNi19-11 |
| SS 310 | 1.4841 | S31000 | SUS 310 | 310S24 | 20Ch25N20S2 | – | X15CrNi25-20 |
| SS 316 | 1.4401 / 1.4436 | S31600 | SUS 316 | 316S31 / 316S33 | – | Z7CND17-11-02 | X5CrNiMo17-12-2 / X3CrNiMo17-13-3 |
| SS 316L | 1.4404 / 1.4435 | S31603 | SUS 316L | 316S11 / 316S13 | 03Ch17N14M3 / 03Ch17N14M2 | Z3CND17‐11‐02 / Z3CND18‐14‐03 | X2CrNiMo17-12-2 / X2CrNiMo18-14-3 |
| SS 317L | 1.4438 | S31703 | SUS 317L | – | – | – | X2CrNiMo18-15-4 |
| SS 321 | 1.4541 | S32100 | SUS 321 | – | – | – | X6CrNiTi18-10 |
| SS 347 | 1.4550 | S34700 | SUS 347 | – | 08Ch18N12B | – | X6CrNiNb18-10 |
| SS 904L | 1.4539 | N08904 | SUS 904L | 904S13 | STS 317J5L | Z2 NCDU 25-20 | X1NiCrMoCu25-20-5 |
KOMPOSISI KIMIA TIUB GEJEL SS
321 keluli tahan karat tiub bergelung 6*1mm
| Gred | C | Mn | Si | P | S | Cr | Mo | Ni | N | Ti | Fe | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Tiub Gegelung SS 304 | min. | 18.0 | 8.0 | |||||||||
| maks. | 0.08 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 10.5 | 0.10 | ||||
| Tiub Gegelung SS 304L | min. | 18.0 | 8.0 | |||||||||
| maks. | 0.030 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 12.0 | 0.10 | ||||
| Tiub Gegelung SS 310 | 0.015 maks | 2 maks | 0.015 maks | 0.020 maks | 0.015 maks | 24.00 26.00 | 0.10 maks | 19.00 21.00 | 54.7 min | |||
| Tiub Gegelung SS 316 | min. | 16.0 | 2.03.0 | 10.0 | ||||||||
| maks. | 0.035 | 2.0 | 0.75 | 0.045 | 0.030 | 18.0 | 14.0 | |||||
| Tiub Gegelung SS 316L | min. | 16.0 | 2.03.0 | 10.0 | ||||||||
| maks. | 0.035 | 2.0 | 0.75 | 0.045 | 0.030 | 18.0 | 14.0 | |||||
| Tiub Gegelung SS 317L | 0.035 maks | 2.0 maks | 1.0 maks | 0.045 maks | 0.030 maks | 18.00 20.00 | 3.00 4.00 | 11.00 15.00 | 57.89 min | |||
| Tiub Gegelung SS 321 | 0.08 maks | 2.0 maks | 1.0 maks | 0.045 maks | 0.030 maks | 17.00 19.00 | 9.00 12.00 | 0.10 maks | 5(C+N) 0.70 maks | |||
| Tiub Gegelung SS 347 | 0.08 maks | 2.0 maks | 1.0 maks | 0.045 maks | 0.030 maks | 17.00 20.00 | 9.0013.00 | |||||
| Tiub Gegelung SS 904L | min. | 19.0 | 4.00 | 23.00 | 0.10 | |||||||
| maks. | 0.20 | 2.00 | 1.00 | 0.045 | 0.035 | 23.0 | 5.00 | 28.00 | 0.25 | |||
SIFAT MEKANIK GEJEL KELULI TAHAN KARAT
321 keluli tahan karat tiub bergelung 6*1mm
| Gred | Ketumpatan | Takat lebur | Kekuatan Tegangan | Kekuatan Hasil (0.2% Offset) | Pemanjangan |
|---|---|---|---|---|---|
| Tiub Gegelung SS 304/ 304L | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi 75000, MPa 515 | Psi 30000 , MPa 205 | 35 % |
| Tiub Gegelung SS 310 | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi 75000, MPa 515 | Psi 30000 , MPa 205 | 40% |
| SS 306 Tiub Gegelung | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi 75000, MPa 515 | Psi 30000 , MPa 205 | 35 % |
| Tiub Gegelung SS 316L | 8.0 g/cm3 | 1399 °C (2550 °F) | Psi 75000, MPa 515 | Psi 30000 , MPa 205 | 35 % |
| SS 321 Tiub Gegelung | 8.0 g/cm3 | 1457 °C (2650 °F) | Psi 75000, MPa 515 | Psi 30000 , MPa 205 | 35 % |
| SS 347 Tiub Gegelung | 8.0 g/cm3 | 1454 °C (2650 °F) | Psi 75000, MPa 515 | Psi 30000 , MPa 205 | 35 % |
| Tiub Gegelung SS 904L | 7.95 g/cm3 | 1350 °C (2460 °F) | Psi 71000, MPa 490 | Psi 32000, MPa 220 | 35 % |
Masa siaran: Mei-08-2023