Aloi Super HASTELLOY(r) C276 (UNS N10276) 6.35*1.65 mm
Komposisi kimia
Aloi Super HASTELLOY(r) C276 (UNS N10276) 6.35*1.65 mm
Komposisi kimia HASTELLOY(r) C276 digariskan dalam jadual berikut.
| unsur | Kandungan (%) |
|---|---|
| Nikel, Ni | 57 |
| Molibdenum, Mo | 15-17 |
| Chromium, Cr | 14.5-16.5 |
| Besi, Fe | 4-7 |
| Tungsten, W | 3-4.50 |
| Kobalt, Co | 2.50 |
| Mangan, Mn | 1 |
| Vanadium, V | 0.35 |
| Silikon, Si | 0.080 |
| Fosfor, P | 0.025 |
| Karbon, C | 0.010 |
| Sulfur, S | 0.010 |
Ciri-ciri fizikal
Aloi Super HASTELLOY(r) C276 (UNS N10276) 6.35*1.65 mm
Jadual berikut menunjukkan sifat fizikal HASTELLOY(r) C276.
| Hartanah | Metrik | Imperial |
|---|---|---|
| Ketumpatan | 8.89 g/cm³ | 0.321 lb/in³ |
| Takat lebur | 1371°C | 2500°F |
Sifat Mekanikal
Aloi Super HASTELLOY(r) C276 (UNS N10276) 6.35*1.65 mm
Sifat mekanikal HASTELLOY(r) C276 dipaparkan dalam jadual berikut.
| Hartanah | Metrik | Imperial |
|---|---|---|
| Kekuatan tegangan (@ketebalan 4.80-25.4 mm, 538°C/@ketebalan 0.189-1.00 in, 1000°F) | 601.2 MPa | 87200 psi |
| Kekuatan hasil (0.2% diimbangi, @ketebalan 2.40 mm, 427°C/@ketebalan 0.0945 in, 801°F) | 204.8 MPa | 29700 psi |
| Modulus anjal (RT) | 205 GPa | 29700 ksi |
| Pemanjangan semasa putus (dalam 50.8 mm, @ketebalan 1.60-4.70 mm, 204°C/@ketebalan 0.0630-0.185 in, 399°F) | 56% | 56% |
| Kekerasan, Rockwell B (plat) | 87 | 87 |
Sifat Terma
Sifat terma HASTELLOY(r) C276 diberikan dalam jadual berikut.
| Hartanah | Metrik | Imperial |
|---|---|---|
| Ko-cekap pengembangan terma (@24-93°C/75.2-199°F) | 11.2 µm/m°C | 6.22 µin/in°F |
| Kekonduksian terma (-168 °C) | 7.20 W/mK | 50.0 BTU in/jam.ft².°F |
Jawatan Lain
Bahan yang setara dengan HASTELLOY(r) C276 adalah seperti berikut.
| ASTM B366 | ASTM B574 | ASTM B622 | ASTM F467 | DIN 2.4819 |
| ASTM B575 | ASTM B626 | ASTM B619 | ASTM F468 | |